MPC-180 is a 100% solid, two component fast curing epoxy coating designed for controlling moisture vapor emissions on new or deteriorated concrete floors. This coating is recommended to be applied in areas of high humidity or on wet concrete. When applied at a thickness of 18 mils, it exceeds ASTM F3010 product requirements for vapor permeance. This coating will withstand moisture vapor emission rates up to 25lbs./24hrs./1000 ft2 when applied properly.
Areas of application
o Industrial Use - Garages; Warehouses; Airports and hangars; Processing and manufacturing plants
o Commercial Use - Shopping malls and boutiques; Hotels; Offices; Showrooms; Restaurants; Hospitals; Schools; Community centers
o ResidentialUse–Entrancesandhallways;basements;entertainmentrooms;bathrooms;kitchens and living rooms; outdoors spaces and pool outlines
Packaging and Recommended Thickness
MPC- 180 is offered in the following kit sizes:
o 2-gallonkit(3.78Lresin(A)and3.78Lhardener(B)) o Bulkpackagingalsoavailableuponrequest
Recommended Film Thickness: 90-100 sq. ft. @ 18mils
Remove dust, dirt, grease, oil and all other contaminants with proper cleaner/degreaser. Prepare the surface mechanically as per ICRI-CSP2 profile by diamond grinding to ensure removal of laitance, curing agents and sealers. The compressive strength of a newly poured concrete substrate must be at least 25 MPA (3635 psi) after 28 days cure and at least 1.5 MPA (218 psi) tensile strength. Be careful with condensation (within 10 degrees of the dew point). All cracks, holes and irregularities must be repaired with our epoxy crack filler prior to applying the coating.
The products must be conditioned between for 18°C (65°F) and 30°C (86°F) prior to application. Pre-mix each component separately for 2-3 minutes each. Open container with 1 part of component A in it, then add the 1 part of component B to it (mixing ratio 1:1). Mix the components for at least 2-3 minutes using a low-speed drill (300-450 rpm) to reduce air entrapment and to obtain a homogeneous mixture.
1. Apply 1st coat of MPC-180 using a rubber squeegee and roll to obtain a uniform coating (using a fine quality 10mm roller).
Clean equipment with xylene. Once the product has hardened, it may only be removed mechanically.
o This coating is not a replacement for a waterproofing membrane.
o This coating does not protect against areas of high hydrostatic pressure.
discoloration (amine blushing)
Health and Safety
Components A and B contain toxic and corrosive ingredients. Consult the safety data sheet (S.D.S) for further information.